The Difference Between Cold Drawn and Extruded Metals



Forming metals into specific shapes can be a challenging process. While metal bars and rods can be formed relatively simply, shapes such as tubes, beams, and various types of channel bar are metal configurations that sometimes require special forming processes to create. Two common metal forming processes used are extrusion and cold drawing. While both are common methods of shaping metal, there are differences between them that should be understood before making a metal purchasing decision.Get more news about Precision Cold Extrusion,you can vist our website!

What is Extrusion?
Extrusion is a metal forming process used to make complex shapes. It involves forcing a metal through one side of a die and having a finished product come out the other side. Extrusion is commonly done to form Aluminum. Extruding metal has several steps that are required.

A metal billet is shaped through smelting, solidifying, and rolling.
The billet is heated up to a temperature suitable for extruding. The heat makes the metal more malleable and easier to form.
Pressure is exerted on the billet against the die. The dies used in extrusion have been precision machined to ensure that a quality piece of extruded metal with acceptable dimensions comes out the other side of the die.
Once the metal is forced through the die, it can be cut to various lengths, coated, annealed, or have any other post-extrusion procedures applied to it.
What is Cold Drawing?
Like extrusion, cold drawing is also used to form complex shapes and requires a metal billet to already be formed prior to beginning the process. However, unlike extrusion, heating the billet is not part of the cold drawing process. Rather than being fed through one die, the metal is fed through a series of molds through the cold drawing process. This is because the metal is less malleable and formable without the addition of heat. The number of dies a billet goes through depends on the complexity and thickness of the final shape. After the billet has been cold drawn to the correct metal shape and size, it is ready for post-processing. Cold Drawing is commonly done to form steel and stainless steel, but can also be used to form aluminum.

Notable during the cold drawing process is that the metal being formed goes through plastic deformation. Care must be taken during the cold drawing process to ensure that excessive plastic deformation doesn’t occur as it can result in tears in the metal or a brittle final product.